Haynes® 282® Alloy
Applications
Compressors, Combustors, Transition liners, Rings, Exhaust/nozzle components, Hot-gas-path components
Description
Haynes® Alloy 282 is an age-hardenable nickel-based superalloy that combines excellent creep strength with thermal stability, weldability, and fabricability. This new alloy has excellent creep strength in the temperature range of 1200 to 1700°F (649-927°C), surpassing that of Waspaloy alloy, and approaching that of R-41 alloy. Haynes® Alloy 282 can be further aged from the annealed condition or cold reduced condition for modest gains in physical properties. Other notable properties include resistance to strain-age cracking and high-temperature oxidation.
Industries Supplied
Aerospace, Land Based Turbines, Automotive
Nominal Composition
C: 0.04 – 0.08
Mn: 0.30 max
Si: 0.15 max
P: 0.015 max
S: 0.015 max
B: 0.003 – 0.010
Ni: Bal min
Cr: 18.5 – 21.5
Co: 9.0 – 11.0
Mo: 8.0 – 9.0
W: 0.5 max
Ti: 1.90 – 2.30
Ta: 0.10 max
Nb: 0.2 max
Al: 1.38 – 1.65
Fe: 1.5 max
Cu: 0.1 max
Zr: 0.020 max
Physical Properties
Density: 0.299 lb/in3, (8.27 g/cm3)
Modulus of Elasticity (E):
At 70°F (20°C): 31.5 x 103 ksi (217 GPa)
Modulus of Rigidity (G):
At 70°F (20°C): 11.9 x 103 ksi (82 GPa)
Coefficient of Expansion:
9.3 µin/in-°F (70-1800°F)
16.9 µm/m-°C (25-1000°C)
Electrical Resistivity: 49.7 µohm-in, (126.1 µohm-cm)
Thermal Conductivity: 72 Btu-in/ft2-hr-°F, (10.3 W/m-°C)
Applicable Specifications
Wire & Bar: AMS 5915, ASTM B637
Typical Mechanical Properties
- Annealed
- Heat Treatment: 2050-2150°F (1120-1177°C)
- Tensile Strength: 110-140 ksi (758-965 MPa)
- Suggested Operating Conditions: Up to 1700°F (927°C)
- Aged
- Heat Treatment: 1850°F for 2 hours, AC / 1450°F for 8 hours, AC
- Tensile Strength: 150 ksi min (1034 MPa)
- Suggested Operating Conditions: Up to 1700°F (927°C)
Haynes® 282® is a registered trademark of Haynes International, Inc.
For further information Contact:
Contact Us
Phone: 1 847 695 1900
Elgiloy Specialty Metals – Wire Products
356 N.Cross Street
Sycamore, IL 60178 USA
Limitation of Liability and Disclaimer of Warranty:
• The content in these data sheets is provided primarily by third-party melting mills and is provided for reference only. It is not intended for engineering or design.
• Applications may be discussed, however, Elgiloy Specialty Metals, a Division of Combined Metals of Chicago L.L.C., does not recommend or endorse any material for any particular end use or application.
• The data included in this data sheet are typical values and may vary.
• Elgiloy Specialty Metals, a Division of Combined Metals of Chicago L.L.C., makes no representations or warranties, express or implied, as to the accuracy, completeness, condition, suitability, performance, fitness for a particular purpose, or merchantability of any information contained in any data sheet.